The need to create lightweight materials with better mechanical properties has led to the use of Fiber Reinforced Composites (FRCs)s in the aerospace and automotive industries. The mechanical behavior of FRCs is heterogeneous, especially in conditions of low-velocity impact (LVI). The impact events cause structural damage, where most of the available literature deals with mono- or bi-composites in controlled situations. This work will present the results of studying the behavior of mono, bi- and tri-hybrids with carbon, glass and Kevlar fiber-reinforced epoxy. The sequences of the laminate stacks, number of plies and laminate thickness in the drop weight testing were across velocities of 1.91 to 3.91 m/s at drop heights of 19 to 79 cm. The dominant pillars of LVI, such as peak load, energy absorption and the modes of damage, were analyzed. The glass-dominated laminates peaked at 5.67 kN, while the Kevlar-dominated laminates reached peak flow in ductile collapse with greater quantities of absorbed energy. The leaders in strength and energy were the hybrids of Kevlar–glass (KG) cross-ply at 8.08 kN and 47.28 J and quasi-isotropic Kevlar–carbon–glass (KCG) at 9.12 kN and 47.25 J, showcasing a balance of strength and toughness. The rest, holding a greater quantity of Kevlar, ranging in thickness and cross-plies, were shaped with a load center. The experimental conclusion is that hybridization improved impact resistance and ductility, which is best supported by the glass/carbon rigidity-layered laminates. Such understanding directs the design work of future composite materials for better impact control.